Characterization of Transparent Conducting Indium Zinc Oxide Thin Films Fabricated by Magnetron Sputtering

ASIA unversity > 資訊學院 > 光電與通訊學系 > 博碩士論文 > Item 310904400/91959

jsp.display-item.identifier=請使用永久網址來引用或連結此文件: http://asiair.asia.edu.tw/ir/handle/310904400/91959

题名:	Characterization of Transparent Conducting Indium Zinc Oxide Thin Films Fabricated by Magnetron Sputtering
作者:	Liu, Chin-Ping
贡献者:	光電與通訊學系
关键词:	Magnetron Sputter system、Indium Zinc Oxide (IZO);Transparent conductive oxide (TCO);Pole Figure
日期:	2015
上传时间:	2015-10-08 01:40:25 (UTC+0)
出版者:	亞洲大學
摘要:	Magnetron Sputtering has been widely used in the process of preparing large area coating. Because of the high and steady sputtering rate and good uniformity of thin films. In addition, select the Indium Zinc Oxide (IZO) transparent conductive oxide films were deposited onto the glass substrate by magnetron sputtering method. Deposition was performed by changing processing conditions, such as oxygen gas flow, process pressure, argon gas flow and after deposition annealing. The structural, optical, electrical and Microstructure properties of IZO films have been characterized by X-ray diffraction, Atomic Force Microscope, Raman Spectroscope, Four Point probe, Hall Effect Measurement System, UV-VIS, Pole Figure, Ellipseometer, TEM, respectively. In IZO process we first change the oxygen content, the resistivity of as low as 0.83×100 Ω•cm, transmittance of about 83 % can be seen in the XRD analysis of In2O3 (222) crystalline phase. Then change argon content resistivity as low as 5.47×10-3 Ω•cm, transmittance of about 80 %, the situation in the XRD analysis of non-crystalline. The last change process pressure resistivity as low as 7.88×10-4 Ω•cm, transmittance of about 81 %, the situation in the XRD analysis of non-crystalline.