Manufacturing Technique and Interfacial Modification of Polypropylene/Short Glass Fiber Composites

ASIA unversity > 創意設計學院 > 時尚設計學系 > 期刊論文 > Item 310904400/81334

請使用永久網址來引用或連結此文件: http://asiair.asia.edu.tw/ir/handle/310904400/81334

題名:	Manufacturing Technique and Interfacial Modification of Polypropylene/Short Glass Fiber Composites
作者:	Jia Horng Lin;Zheng Lan Lin;Jin Mao Chen;Ching Wen Lou
貢獻者:	時尚設計學系
日期:	2014-03
上傳時間:	2014-10-08 06:02:33 (UTC+0)
摘要:	Maleic anhydride grafted polypropylene (PP-g-MA) is used as a coupling agent, and the influence of its used amount on the mechanical properties of the polypropylene/short glass fiber (PP/SGF) composites is examined. 1, 2, and 3 wt% of PP-g-MA is separately added to PP/SGF composites that are made at an 80/20 ratio (wt%), made into pellets on a single screw extruder, and then made into test samples on an injection machine. When PP-g-MA increases from 1 wt% to 3 wt%, the tensile strength of the PP/SGF composites increases from 56.22 MPa to 64.85 MPa; likewise, flexural strength increases from 67.29 MPa to 81.24 MPa, and Izod impact strength increases from 197.70 J/m 269.61 J/m. SEM images show that the surface of SGF are encapsulated with a layer of PP matrix, which indicates that PP-g-MA can effectively improve the interfacial adhesion between PP and SGF and thus increase the mechanical properties of the resulting composites.
關聯:	Advanced Materials Research
顯示於類別:	[時尚設計學系] 期刊論文

文件中的檔案:

檔案	大小	格式	瀏覽次數
index.html	0Kb	HTML	394	檢視/開啟

在ASIAIR中所有的資料項目都受到原著作權保護.